Stainless steel pipe cap: 304 304L 316 316L 321 2520 310, 317, etc Diameter: dn15-dn1200 Wall thickness: sch5-sch160 Standard: ASME DIN JIS BS GB / T JB sh Hg, as follows: GB / t12459-2017, GB / t13401-2017, ASME B16 9,SH3408, SH3409,HG/T21635,DL/T695,SY/T0510, DIN2617 Uses: water, beverage, beer, food, petrochemical industry, nuclear power, machinery, medical equipment, chemical fertilizer, shipbuilding, waterproof treatment, pipeline, etc Packing: wooden case, carton Avoid splicing at r of dished pipe cap, which will reduce thickness and high stress. During splicing, only radial and circumferential weld directions are allowed. This requirement may be cancelled for large pipe caps in the future. The splicing distance shall be greater than 3 δ, And not less than 100mm (the welding heat affected zone is a high stress zone, and the chemical composition in this zone will be burned. Therefore, it is necessary to avoid the high stress area, which is related to the thickness. According to practical experience, the stress attenuation length is greater than 3 δ, And not less than 100mm). However, refrigeration equipment is difficult to meet this requirement, which has its particularity. For the cap formed after splicing, the splicing weld shall be subject to 100% radiographic or ultrasonic testing, and the qualification level shall follow the equipment shell.
Forging method. Machining flanges through forging can be divided into two types: free forging and die forging. Free forging involves compression processing under a forging press